I-Silicon carbide wafer boat iyithuluzi elithwala imithwalo lama-wafers, elisetshenziswa kakhulu kuzinqubo zokusabalalisa ilanga ne-semiconductor. Inezici ezifana nokumelana nokugqoka, ukumelana nokugqwala, ukumelana nomthelela wokushisa okuphezulu, ukumelana nokuqhuma kwamabhomu e-plasma, izinga lokushisa eliphezulu elithwala amandla, ukushisa okuphezulu kwe-thermal, ukuchithwa kokushisa okuphezulu, nokusetshenziswa isikhathi eside okungelula ukugoba nokukhubazeka. Inkampani yethu isebenzisa impahla ye-silicon carbide ehlanzekile kakhulu ukuze iqinisekise impilo yesevisi futhi ihlinzeka ngemiklamo eyenziwe ngokwezifiso, okuhlanganisa isikebhe esilucwecwana esime mpo nesivundlile.
I-Material Datasheet
| 材料Okubalulekile | I-R-SiC |
| 使用温度Izinga lokushisa lokusebenza (°C) | 1600°C ( 氧化气氛Indawo enezinsimbi)1700°C ( 还原气氛Indawo yokunciphisa) |
| Okuqukethwe kwe-SiC含量SiC (%) | > 99 |
| 自由Si 含量Okuqukethwe kwamahhala kwe-Si (%) | <0.1 |
| 体积密度Ukuminyana ngobuningi (g/cm3) | 2.60-2.70 |
| 气孔率I-porosity ebonakalayo (%) | < 16 |
| 抗压强度Amandla okuchoboza (MPa) | > 600 |
| 常温抗弯强度Amandla okugoba okubandayo (MPa) | 80-90 (20°C) |
| 高温抗弯强度Amandla okugoba ashisayo (MPa) | 90-100 (1400°C) |
| 热膨胀系数 I-coefficient yokunweba okushisayo @1500°C (10-6/°C) | 4.70 |
| 导热系数I-Thermal conductivity @1200°C (W/m•K) | 23 |
| 杨氏模量I-Elastic modulus (GPa) | 240 |
| 抗热震性Ukumelana nokushaqeka okushisayo | 很好Kuhle ngokwedlulele |
Inkampani engu-Ningbo VET Energy Technology Co., Ltdiyibhizinisi lobuchwepheshe obuphezulu eligxile ekukhiqizeni nasekuthengisweni kwezinto ezisezingeni eliphezulu, izinto zokwakha kanye nobuchwepheshekuhlanganisei-graphite, i-silicon carbide, i-ceramics, ukwelashwa kwendawo nokunye. Imikhiqizo isetshenziswa kabanzi ku-photovoltaic, semiconductor, amandla amasha, i-metallurgy, njll.
Ithimba lethu lezobuchwepheshe livela ezikhungweni eziphezulu zocwaningo lwasekhaya, linganikeza izixazululo zezinto ezibonakalayo ezinobuchwepheshekwakho.
Siyakwamukela ngokufudumele ukuthi uvakashele ifekthri yethu, ake sibe nengxoxo eyengeziwe!