Awọn ẹya akọkọ ti igbona graphite:
1. uniformity ti alapapo be.
2. ti o dara itanna elekitiriki ati ki o ga itanna fifuye.
3. ipata resistance.
4. inoxidizability.
5. ga kemikali ti nw.
6. ga darí agbara.
Awọn anfani ni agbara daradara, ga iye ati kekere itọju. A le gbe awọn egboogi-ifoyina ati ki o gun aye igba lẹẹdi crucible, lẹẹdi m ati gbogbo awọn ẹya ara ti lẹẹdi ti ngbona.
Main sile ti lẹẹdi ti ngbona
| Imọ Specification | Semicera-M3 |
| Ìwọ̀n Ọ̀pọ̀lọpọ̀ (g/cm3) | ≥1.85 |
| Akoonu Eeru (PPM) | ≤500 |
| Eti okun Lile | ≥45 |
| Atako pato (μ.Ω.m) | ≤12 |
| Agbara Flexural (Mpa) | ≥40 |
| Agbara Ipilẹṣẹ (Mpa) | ≥70 |
| O pọju. Iwon ọkà (μm) | ≤43 |
| Olùsọdipúpọ ti Gbona Imugboroosi Mm/°C | ≤4.4*10-6 |
Agbara VET jẹ awọnolupese gidi ti graphite ti adani ati awọn ọja ohun alumọni carbide pẹlu ibora CVD,le peseorisirisiawọn ẹya adani fun semikondokito ati ile-iṣẹ fọtovoltaic. OẸgbẹ imọ-ẹrọ ur wa lati awọn ile-iṣẹ iwadii ile ti o ga julọ, le pese awọn solusan ohun elo alamọdaju diẹ siifun e.
A ṣe idagbasoke awọn ilana ilọsiwaju nigbagbogbo lati pese awọn ohun elo ilọsiwaju diẹ sii,atiti ṣiṣẹ imọ-ẹrọ itọsi iyasọtọ, eyiti o le jẹ ki isunmọ laarin ibora ati sobusitireti ṣinṣin ati ki o kere si isọkuro.
Founjẹ ti awọn ọja wa:
1. Agbara ifoyina iwọn otutu to gaju to 1700℃.
2. Ga ti nw atigbona uniformity
3. O tayọ ipata resistance: acid, alkali, iyo ati Organic reagents.
4. Lile giga, dada iwapọ, awọn patikulu ti o dara.
5. Gigun iṣẹ igbesi aye ati diẹ sii ti o tọ
| CVD SiC薄膜基本物理性能 Awọn ohun-ini ti ara ipilẹ ti CVD SiCti a bo | |
| 性质 / Ohun ini | 典型数值 / Aṣoju Iye |
| 晶体结构 / Crystal Be | FCC β ipele多晶，主要为（111)取向 |
| 密度 / iwuwo | 3.21 g/cm³ |
| 硬度 / Lile | 2500 维氏硬度 (ẹrù 500g) |
| 晶粒大小 / Ọkà SiZe | 2 ~ 10μm |
| 纯度 / Kemikali ti nw | 99.99995% |
| 热容 / Ooru Agbara | 640 · kg-1· K-1 |
| 升华温度 / Sublimation otutu | 2700 ℃ |
| 抗弯强度 / Agbara Flexural | 415 MPa RT 4-ojuami |
| 杨氏模量 / Young's Modul | 430 Gpa 4pt tẹ, 1300 ℃ |
| 导热系数 / ThermalIwa ihuwasi | 300W·m-1· K-1 |
| 热膨胀系数 / Imugboroosi Gbona (CTE) | 4.5×10-6K-1 |