Anode Mu'i Fa'a'ai Mu'ai Fa'amea Anode mo Alumini Electrolysis

Anode mua'i tao mua'i taoina anode mo alumini Electrolysis Ata Fa'aalia

Fa'amatalaga Puupuu:

Fa'amatalaga Oloa

Faailoga o oloa

Tulaga lelei:
1.CO2 Reactivity Residue e mafai ona oʻo atu i luga aʻe o le 91%, Air Reactivity e mafai ona oʻo i luga aʻe o le 96%; o le ola-span i sela o le alumini electrolysis o 30-33days.

2. Higher te'i vevela Resistance
Fa'aaliga vevela: <4*10
Fa'avevela vevela : <3W/mkl

3.higher density i le taimi nei
mamafa o iai nei: > 0.8A/cm2
4.lower Resistivity eletise
Tete'e eletise: 55-56μΩm

ANODE FAAMATALAGA

Fa'asologa	MEATOAGA	Vaega	Auala masani	Avanoa
1	Moni Moni	g/cm3	ISO 8004	2 Min
2	E aliali mai le To'o	g/cm3	ISO 12985	1.52-1.58
3	Malosi o le ea	npm	ISO 15906	0.5-1.5
5	Malosi Compressive	N/mm2	ISO 18515	40-48
6	Youngs moudle	Gpa	ISO 12989	4-5.5
7	Malosi Fa'asusu	N/mm2	ISO 12986	8 – 10
8	Spe. Elec. Tete'e	µΩm	ISO 11713	55-62
9	Cof. Lin . Mafanafana	µm/(km)	ISO 14420	3.75-4.5
10	Amioga vevela	W/(km)	ISO 129087	3-4.5
11	ASh	%	ISO 8005	0.5 Max
12	Ea Reactivity toega pefu leiloa	% % %	ISO 12989-1	75 – 85 4 – 8 10 – 20
13	Co2 Reactivity toega pefu leiloa	% % %	ISO 12988-1	84 – 95 3 – 8 6 – 14
14	Elemene S V Fe F Ca Al Ni SI	% ppm // // // // //	ASTM D6376	0.5 – 2.5 30 – 320 100 – 600 150 – 600 50 – 200 150 – 600 40 – 200 50 – 300