Pre-Baked Anode Pre-Baking Anode fun Aluminiomu Electrolysis

Alaye ọja

Anfani:
1.CO2 Reactivity Residue le de ọdọ 91%, Air Reactivity le de ọdọ 96%; igbesi aye-aye ninu awọn sẹẹli ti aluminiomu electrolysis jẹ 30-33days.

2.Higher gbona mọnamọna Resistance
Ifihan igbona: <4*10
Ṣiṣẹda Ooru: <3W/mkl

3.higher lọwọlọwọ iwuwo
lọwọlọwọ iwuwo:> 0.8A/cm2
4.lower Electrical Resistivity
Itanna Resistivity: 55-56μΩm

ANODE PATAKI

jara	ONÍNÌYÀN	Ẹyọ	Standard ọna	Ibiti o
1	Iwuwo gidi	g/cm3	ISO 8004	2 Min
2	Iwuwo ti o han gbangba	g/cm3	ISO 12985	1.52-1.58
3	Afẹfẹ permeability	npm	ISO 15906	0.5-1.5
5	Agbara titẹ	N/mm2	ISO 18515	40-48
6	odo moudle	Gpa	ISO 12989	4-5.5
7	Agbara Flexural	N/mm2	ISO 12986	8 – 10
8	Spe. Elec. Atako	µΩm	ISO 11713	55-62
9	Cof. Lin . Gbona	µm/(km)	ISO 14420	3.75-4.5
10	Gbona Conductivity	W/(km)	ISO 129087	3-4.5
11	Ash	%	ISO 8005	0.5 ti o pọju
12	Air Reactivity aloku eruku Ti sọnu	% % %	ISO 12989-1	75 – 85 4 – 8 10 – 20
13	Co2 Reactivity iyokù eruku sọnu	% % %	ISO 12988-1	84 – 95 3 – 8 6 – 14
14	Awọn eroja S V Fe F Ca Al Ni SI	% ppm // // // // //	ASTM D6376	0.5 - 2.5 30 – 320 100 – 600 150 – 600 50 – 200 150 – 600 40 – 200 50 – 300