Pre-Baked Anode Pre-Baking Anode no ka Aluminum Electrolysis

Pre-Baked Anode Pre-Baking Anode no Aluminum Electrolysis Kiʻi Hōʻikeʻike

ʻO ka wehewehe pōkole:

E hoʻouna i ka leka uila iā mākou Hoʻoiho ma ke ʻano he PDF

Huahana Huahana

Pōmaikaʻi:
1.CO2 Reactivity koena hiki ke piʻi ma luna o 91%, Air Reactivity hiki ke piʻi ma luna o 96%;ʻo ke ola-span i loko o nā pūnaewele o ka alumini electrolysis he 30-33days.

2.Higher thermal ha'alulu Kū'ē
Hōʻike wela: <4*10
Hoʻolawe wela : <3W/mkl

3.ʻoi aku ka nui o kēia manawa
ka nui o kēia manawa: > 0.8A/cm2
4.lower uila Resistivity
Ke kū'ē uila: 55-56μΩm

ANODE SPECIFICATION

moʻo	WAIWAI	Unite	ʻano maʻamau	Laulā
1	ʻOiʻoi loa	g/cm3	ISO 8004	2 Min
2	ʻIke ʻia ʻo Density	g/cm3	ISO 12985	1.52-1.58
3	Hiki i ka ea	npm	ISO 15906	0.5-1.5
5	Ka ikaika hoʻopili	N/mm2	ISO 18515	40-48
6	ʻŌpio moudle	Gpa	ISO 12989	4-5.5
7	Ikaika Flexural	N/mm2	ISO 12986	8 – 10
8	ʻO Spe. Ua haʻi aku ʻo Elec. Kūʻē	µΩm	ISO 11713	55-62
9	Ua haʻi aku ʻo Cof. Lin . Māmā	µm/(km)	ISO 14420	3.75-4.5
10	ʻO ka hoʻoili wela	W/(km)	ISO 129087	3-4.5
11	ASh	%	ISO 8005	0.5 Max
12	Ke koena o ka ea lepo Nalo	% % %	ISO 12989-1	75 – 85 4 – 8 10 – 20
13	Co2 Reactivity koena lepo nalowale	% % %	ISO 12988-1	84 – 95 3 – 8 6 – 14
14	ʻElemu S V Fe F Ca Al Ni SI	% ppm // // // // //	ASTM D6376	0.5 – 2.5 30 – 320 100 – 600 150 – 600 50 – 200 150 – 600 40 – 200 50 – 300