Anode Mua-Baked Pre-Baking Anode mo te Hiko Konumohe

Anode Mua-Baked Pre-Baking Anode mo te Aluminium Electrolysis Whakaahua Whakaatu

Whakaahuatanga Poto:

Tukuna he imeera ki a matou Tikiake hei PDF

Taipitopito Hua

Tohu Hua

Painga:
1.CO2 Reactivity Reactivity Ka taea te eke ki runga ake i te 91%, Ka taea e te Air Reactivity te eke ki runga ake i te 96%;ko te roa o te ora i roto i nga ruma o te electrolysis konumohe ko 30-33days.

2.Higher waiariki ru Ātete
Te Maranga Weariki : <4*10
Te Whakawhiti Wera : <3W/mkl

3.higher kiato o nāianei
kiato o nāianei: > 0.8A/cm2
4.lower Hiko Resistivity
Te Whakaaetanga Hiko: 55-56μΩm

WHAKAMAHI ANODE

Rangatū	WHAI	Waeine	Tikanga paerewa	Awhe
1	Tino Totoi	g/cm3	ISO 8004	2 Min
2	Te Totoi Te ahua	g/cm3	ISO 12985	1.52-1.58
3	Te uruhanga o te hau	npm	ISO 15906	0.5-1.5
5	Te Kaha Kōpeke	N/mm2	ISO 18515	40-48
6	Nga rangatahi moudle	Gpa	ISO 12989	4-5.5
7	Te Kaha Toka	N/mm2	ISO 12986	8 – 10
8	Spe. Ko te Elec. Ātete	µΩm	ISO 11713	55-62
9	Cof. Lin . Ngawha	µm/(km)	ISO 14420	3.75-4.5
10	Te Whakawhitinga Ngawha	W/(km)	ISO 129087	3-4.5
11	ASh	%	ISO 8005	0.5 Max
12	Te toenga tauhohenga o te hau puehu Kua ngaro	% % %	ISO 12989-1	75 – 85 4 – 8 10 – 20
13	Co2 Reactivity toenga puehu ngaro	% % %	ISO 12988-1	84 – 95 3 – 8 6 – 14
14	Huānga S V Fe F Ca Al Ni SI	% ppm // // // // //	ASTM D6376	0.5 – 2.5 30 – 320 100 – 600 150 – 600 50 – 200 150 – 600 40 – 200 50 – 300