The CFC guide rails are mainly used to support and guide heating elements or workpieces in high-temperature furnaces.
The main functions includes:
1.Supporting structure:
The CFC guide rail provide stable support for heating elements or workpieces in furnace.
2.Guidance function:
The CFC guide rail help to accurately guide the movement of the workpiece.
3.High temperature resistance:
The carbon carbon materials have excellent high-temperature resistance and can maintain their physical and chemical properties at extreme temperatures.
4.Thermal conduction:
Carbon carbon guide rails have good thermal conductivity, which helps to evenly conduct heat and improve heating efficiency.
5. Weight Reduction:
Carbon carbon materials are relatively lightweight, helping to reduce the overall weight of equipment and facilitating operation and installation.
VET Energy is specialized in high-performance carbon-carbon composite customized components, we provide comprehensive solutions from material formulation to finished products manufacturing. With complete capabilities in carbon fiber preform preparation, chemical vapor deposition, and precision machining, our products are widely used in semiconductor, photovoltaic, and high-temperature industrial furnace applications.
Technical Data of Carbon-Carbon Composite |
||
| Index | Unit | Value |
| Bulk density | g/cm3 | 1.40~1.50 |
| Carbon content | % | ≥98.5~99.9 |
| Ash | PPM | ≤65 |
| Thermal conductivity (1150℃) | W/m.k | 10~30 |
| Tensile strength | Mpa | 90~130 |
| Flexural Strength | Mpa | 100~150 |
| Compressive strength | Mpa | 130~170 |
| Shear strength | Mpa | 50~60 |
| Interlaminar Shear strength | Mpa | ≥13 |
| Electric resistivity | Ω.mm2/m | 30~43 |
| Coefficient of Thermal Expansion | 106/K | 0.3~1.2 |
| Processing Temperature | ℃ | ≥2400℃ |
| Military quality, full chemical vapor deposition furnace deposition, imported Toray carbon fiber T700 pre-woven 3D needle knitting. Material specifications: maximum outer diameter 2000mm, wall thickness 8-25mm, height 1600mm | ||